Hardness, Insulation, Thermal Conductivity Alumina Ceramic Metal Bonding Metallization Tube Pipe
Description:
The technic of Ceramic Metallization is: adhere one layer of metal film to the ceramic surface, in order to carry out
the welding between ceramic and metal.
The material of ceramic part is 96 alumina, forming methods are dry pressing and CIP.
Product size is precise, little warp; joint strength between metal and ceramic is high; the joint area is close.
1. Material: 95%~99% AL2O3
2. Method of molding: thermal casting, CIP
3. Color: white, Ivory White
4. Sintering temperature: 1600~1750℃
5. Surface finish: Ra0.4&simRa0.8&mum
6. Packing: Pack with carton and ship with wooden case
7. Produce products according to molds or drawings provided by the client and quote according the data of the
products
8. The mould fee of the non-standard products: According the quotation of product
Applications:
Alumina ceramics with superior strength, hardness, insulation, thermal conductivity, high temperature, oxidation
resistance, corrosion resistance, abrasion resistance, high temperature strength and other characteristics, it has
been widely used in engineering, mechanical seals, electronics, instrumentation, sensing, transport,
communications, and other occasions or areas. The content of 99.7%, 99%, 95% alumina products contains the
crucible, sockets, valves, electrodes, spools, wear board, alumina balls, electronic porcelain, textile porcelain
pieces, and other shaped pieces.
Specifications:
95%,99%,99.7% Al2O3 Material Parameters:
Item | Test Condition | Unit Symbol | 95%Alumina ceramics | 99%Alumina ceramics | 99.7%Alumina ceramics |
The main chemical ingredient | Al2O3 | Al2O3 | Al2O3 | ||
Bulk Density | g/cm3 | 3.6 | 3.89 | 3.96 | |
Maximum Use Temperature | 1450℃ | 1600℃ | 1650℃ | ||
Water absorption | % | 0 | 0 | 0 | |
ROHS Hardness | ≥85 | ≥89 | ≥89 | ||
Flexural strength | 20° C | MPa (psi x 103) | 358 (52) | 550 | 550 |
Compressive Strength | 20° C | MPa (psi x 103) | 2068 (300) | 2600(377) | 2600(377) |
Fracture Toughness | K(I c) | Mpa m1/2 | 4-5 | 5.6 | 6 |
Coefficient of thermal expansion | 25-1000° C | 1X 10-6/°C | 7.6 | 7.9 | 8.2 |
Coefficient of thermal conductivity | 20° C | W/m °K | 16 | 30.0 | 30.4 |
Thermal Shock Resistance | Tc | °C | 250 | 200 | 200 |
Dielectricity constant | 1MHz.25℃ | 9 | 9.7 | 9.7 | |
Dielectric strength | ac-kV/mm (ac V/mil) | 8.3 (210) | 8.7 (220) | 8.7 (220) | |
Volume Resistivity | 100℃ | ohm-cm | > 1013 | > 1014 | > 1014 |
![]() |
Hardness, Insulation, Thermal Conductivity Alumina Ceramic Metal Bonding Metallization Tube Pipe Images |